AQUAMER® HB INVISIBLE Hybrid Polymer Based Transparent Coating

 

Description:
Single component, ready-to-use, high technology transparent coating and waterproofing fluid material. It is produced with silane terminated hybrid polymer technology, resistant to UV and does not contain solvent and isocyanate. Suitable for light pedestrian traffic.
Application Areas:
• Indoor and outdoor
• Balconies and terrace roofs with light pedestrian traffic
• Balconies and terraces covered with glazed tiles, ceramics, natural stone, marble, floor tiles, to provide waterproofing without changing the appearance of the material
• Reinforced concrete, plaster and screed • Covering cracks up to 2 mm
• Mosaics and mosaic tiles
• Glass and glass brick
• Metals such as iron, steel and aluminum
• Roof coverings such as CTP, PVC and polycarbonate
• Wet areas such as bathrooms and kitchens
• Potable water tanks, pools and cisterns
• Parquet, wooden doors and window frames to protect coating and waterproofing material
• Joint combinations of all of the materials recommended above.
Advantages:
• Decorative and allows waterproofing without damaging the existing coating and changing
the appearance of the lower covering, as it is transparent
• Does not cause color changes due to oil bleeding on materials such as natural stone or
marble, as it does not contain silicone oil or plastifiers
• Resistant to the abrasion caused by light pedestrian traffic in terraces and balconies
• Bonds even on damp surfaces without primer, provides high adherence
• Resistant to UV, does not crack, sag or turn to yellow. Can be safely used outdoor
• Does not contain solvent and isocyanate which are harmful to human health and to the
environment. Can be safely used indoor and in contact with potable water
• Has medium flexibility, continues to adhere, cover and protect the building from the cracks
formed and grown in joints of roof etc. due to the movements of the buildings, without losing its technical properties, after being cured. Turns to its original form
• Has 100% elastomeric composition; does not shrink as it does not contain solvent
• Almost odorless
• Easily and quickly applied with brush or roller. Does not form seams • Protects its elasticity even in low temperatures, after being cured.
Consumption:
To prevent surfaces from dusting and from dirt: appr. 0.2 kg/m2 in single layer Non-absorbent
surfaces (tiles, ceramics): appr. 0.7 kg/m2 (2 x 0.35 kg/m2 ) in 2 layers Absorbent surfaces (concrete, wood, natural stone): appr. 1.0 kg/m2 (3 x 0.35 kg/m2 ) in 3 layers
Packaging:
1 kg tin cans 5 kg plastic buckets (5 kg aluminum foiled package)

Technical Properties

Appearance : Transparent liquid coating
Density : 1.10 ± 0.05 kg/L Application
Temperature : Between +5°C and +35°C
Hardness (Shore D) : 35 ± 5
Elongation at Break : > 100% (7 days)
Film Formation Time : 60 ± 30 minutes
Curing Rate : 1 mm / 24 hours